High-chromium wear-resistant alloy
| Alloy | Common Heat Treat Condition | Commonly Casted Specs |
|---|---|---|
| A532 Class I Type A | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 Ni-Cr-Hc |
| A532 Class I Type B | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 Ni-Cr-Lc |
| A532 Class I Type C | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 Ni-Cr-GB |
| A532 Class I Type D | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 Ni-HiCr |
| A532 Class II Type A | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 12% Cr |
| A532 Class II Type B | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 15% Cr-Mo |
| A532 Class II Type D | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 20% Cr-Mo |
| A532 Class III Type A | As-Cast ,Hardened HRC≥56 or 59 | ASTM A532 25% Cr |
| EN-GJN-HB340, DIN 5.5600 | HBW min 340 | DIN 12513 ，EN12513 |
| EN-GJN-HB400, DIN 5.5601 | HBW min 400 | DIN 12513 ，EN12513 |
| EN-GJN-HB480, DIN 5.5602 | HBW min 480 | DIN 12513 ，EN12513 |
| EN-GJN-HB500, DIN 5.5603 | HBW min 500 | DIN 12513 ，EN12513 |
| EN-GJN-HB510, DIN 5.5604 | HBW min 510 | DIN 12513 ，EN12513 |
| EN-GJN-HB555, DIN 5.5605 | HBW min 555 | DIN 12513 ，EN12513 |
| EN-GJN-HB630, DIN 5.5606 | HBW min 630 | DIN 12513 ，EN12513 |
| EN-GJN-HB555(XCr11) , DIN 5.5607, EN-JN3019 | HBW min 550, HV min 600 | DIN 12513 ，EN12513 |
| EN-GJN-HB555(XCr14) ,DIN 5.5608, EN-JN3029 | HBW min 550, HV min 600 | DIN 12513 ，EN12513 |
| EN-GJN-HB555(XCr18) ,DIN 5.5609, EN-JN3039 | HBW min 550, HV min 600 | DIN 12513 ，EN12513 |
| EN-GJN-HB555(XCr23) ,DIN 5.5610, EN-JN3049 | HBW min 550, HV min 600 | DIN 12513 ，EN12513 |